| Aligned | Random | Biomimetic |
---|---|---|---|
Ultimate Stress (MPa) | |||
 Parallel | 12.9 ± 4.3*, *** | 3.4 ± 1.1*** | 8.5 ± 1.9*, *** |
 Perpendicular | 1.2 ± 0.3**** | 3.8 ± 1.0*** | 5.1 ± 1.0*** |
Ultimate Strain (mm/mm) | |||
 Parallel | 0.40 ± 0.03* | 3.28 ± 1.49**** | 0.34 ± 0.08 |
 Perpendicular | 3.69 ± 1.30 | 3.00 ± 1.46 | 0.40 ± 0.07*** |
Modulus (MPa) | |||
 Parallel | 93.6 ± 33.9*, ***** | 16.9 ± 9.7 | 68.7 ± 14.7*, ***** |
 Perpendicular | 2.7 ± 0.5*** | 18.5 ± 5.4*** | 39.4 ± 11.6**** |
Yield Stress (MPa) | |||
 Parallel | 4.9 ± 1.5*, ***** | 1.7 ± 0.5 | 4.0 ± 1.3**, ****** |
 Perpendicular | 0.4 ± 0.1**** | 1.7 ± 0.4*** | 2.2 ± 0.4*** |
Yield Strain (mm/mm) | |||
 Parallel | 0.06 ± 0.01***** | 0.11 ± 0.04 | 0.07 ± 0.01***** |
 Perpendicular | 0.12 ± 0.07 | 0.10 ± 0.04 | 0.07 ± 0.02 |